Premium Corundum Firing Plate
Description:
Corundum Firing Plate is a high-quality, durable plate made from corundum (aluminum oxide), specifically designed for use in high-temperature applications such as sintering, calcination, and material processing in muffle furnaces and other laboratory furnaces.
Corundum, with its high melting point and excellent thermal stability, is ideal for withstanding extreme temperatures, typically up to 1700°C or more.
Dimensions: 100×100×15mm
Wall Thickness: 9mm
Alumina Purity: >95%
Continuous operating temperature: ≤1600°C
The corundum firing plate can be used as a support or a saggar.
Multiple plates can be stacked or combined to form a complete furnace set.
We offer customized services according to your requirements!
If you need more detailed information, please contact us immediately. We offer free quotes on all products!
How to Use Alumina Firing Plate?
1. Before the first use, preheat the alumina plate in an oven at around 105°C for 120 minutes to remove moisture.
2. Do not directly heat the alumina plate with gasoline blowtorch, acetylene torch, or alcohol burner to avoid uneven heating and cracking of the product.
3. The heating or cooling rate should not be too fast. The temperature change below 1200°C should be <5°C/minute, and above 1200°C should be ≤4°C/minute.
4. The distance between the product and the heating element (such as carbon tube, silicon molybdenum rod, or heating wire, etc.) should be >2cm.
5. The bottom of alumina plate should preferably not directly contact the bottom of the furnace. It is recommended to use alumina foot pads or other heat-resistant materials to lift the alumina plate, forming air convection to prolong the service life of the product.
Corundum Firing Plate Related Products:
99% High-Purity Alumina Firing Plate
Alumina Kiln Furniture for Muffle Furnace
Square Alumina Crucibles for Muffle Furnace
Square Crucible with Lid for Muffle Furnace
Alumina (Al2O3) Plates with Holes
Get In Touch
Fill out the form below — free quote and professional suggestion will be sent for reference very soon!